Synthesis Structural and Optical Properties Of (Co, Al) co-doped ZnO Nano Particles

International Conference on Advances in Materials and Manufacturing Applications 2017

Swapna, P.^1 ; Venkatramana Reddy, S.^1

Department of Physics, Sri Venkateswara University, Tirupati, Andhra Pradesh

517 502, India^1

关键词: Chemical co-precipitation;    Hexagonal wurtzite;    Secondary phasis;    Stabilizing agents;    Structural and optical properties;    UV-Vis NIR;    UV-VIS-NIR spectra;    Zinc vacancy;   

Others  :  https://iopscience.iop.org/article/10.1088/1757-899X/310/1/012011/pdf
DOI  :  10.1088/1757-899X/310/1/012011

来源: IOP

【 摘 要 】

We prepared (Co, Al) co-doped ZnO nanostructures using the method chemical co-precipitation successfully, at room temperature using PEG (Poly ethylene glycol) as stabilizing agent. Samples are prepared with different concentrations by keeping aluminium at 5 mol percent constant and varying the concentration of cobalt from 1 to 5 mol percent. After the preparation all the samples are carefully subjected to characterizations such as XRD, SEM with EDS, TEM, PL and UV-VIS-NIR. XRD pattern shows that all the samples possess hexagonal wurtzite crystal structure having no secondary phases pertaining to Al or cobalt, which shows successful dissolution of the dopents. TEM results shows the accurate size of particles and is confirmed the XRD data. SEM images of all the samples shows that particles are in nearly spherical shape, EDS spectrum reveals that incorporation of cobalt and aluminum in host lattice. PL spectrum shows that all the samples containing two prominent peaks centered at 420 nm and 446 nm. UV-VIS-NIR spectra has shown three absorptions peaks in the range of wavelength 550 nm to 700 nm, which are ascribed as typical d-d transitions of cobalt ions.