Influence of manufacturing parameters on the strength of PLA parts using Layered Manufacturing technique: A statistical approach | |
Jaya Christiyan, K.G.^1 ; Chandrasekhar, U.^2 ; Rajesh Mathivanan, N.^3 ; Venkateswarlu, K.^4 | |
M S Ramaiah Institute of Technology, Bangalore | |
560054, India^1 | |
Vel-Tech University, Chennai | |
600062, India^2 | |
P e S Institute of Technology, Bangalore | |
560 085, India^3 | |
CSIR-National Aerospace Laboratories, Bangalore | |
560017, India^4 | |
关键词: 3-D printing; Manufacturing parameters; Manufacturing techniques; Nozzle diameter; Point load tests; Poly lactic acid; Processing parameters; Statistical approach; | |
Others : https://iopscience.iop.org/article/10.1088/1757-899X/310/1/012134/pdf DOI : 10.1088/1757-899X/310/1/012134 |
|
来源: IOP | |
【 摘 要 】
A 3D printing was successfully used to fabricate samples of Polylactic Acid (PLA). Processing parameters such as Lay-up speed, Lay-up thickness, and printing nozzle were varied. All samples were tested for flexural strength using three point load test. A statistical mathematical model was developed to correlate the processing parameters with flexural strength. The result clearly demonstrated that the lay-up thickness and nozzle diameter influenced flexural strength significantly, whereas lay-up speed hardly influenced the flexural strength.