会议论文详细信息
International Conference on Mechanical Engineering and Applied Composite Materials | |
Structure and Properties of Melt-spun Bio-based Polyamide/Eu(TTA)3Phen Composite fibers | |
机械制造;材料科学 | |
Li, Yunye^1 ; Lou, Pengfei^2 ; Jia, Qingxiu^1,2 | |
School of Material Science and Engineering, Beijing Institute of Fashion Technology, Beijing | |
100029, China^1 | |
Beijing Engineering Research Center of Textile Nanofiber, Beijing | |
100029, China^2 | |
关键词: Average diameter; Bio-based monomers; Breaking strength; Composite fibers; Coordination bonds; Europium complex; N ,N-Dimethylformamide; Structure and properties; | |
Others : https://iopscience.iop.org/article/10.1088/1757-899X/307/1/012067/pdf DOI : 10.1088/1757-899X/307/1/012067 |
|
学科分类:材料科学(综合) | |
来源: IOP | |
【 摘 要 】
In this paper, the bio-based polyamide (PA ) was melt polymerized from four bio-based monomers. Composites of the bio-based PA and europium complex Eu(TTA)3Phen were prepared through solution mixing using N, N-Dimethylformamide (DMF) and formic acid as the mixed solvent, and then composite fibers were obtained by melt spinning method. The structure and properties of the melt-spun composite fibers were characterized by FTIR and SEM. The results indicated that the Eu(TTA)3Phen complex, with the average diameter below 300 nm, was homogeneously dispersed in the PA matrix. FTIR spectra indicated that the coordination bond between carbonyl of BDIS and Eu(TTA)3Phen complex formed, which was also confirmed by the mechanical properties. The initial modulus and breaking strength of these fibers can arrived at 2.5GPa and 0.3GPa, respectively.【 预 览 】
Files | Size | Format | View |
---|---|---|---|
Structure and Properties of Melt-spun Bio-based Polyamide/Eu(TTA)3Phen Composite fibers | 237KB | download |