Polypropylene Oil as a Fuel for Ni-YSZ | YSZ | LSCF Solid Oxide Fuel Cell

International Conference on Chemistry and Material Science 2017

化学;材料科学

Pratiwi, Andini W.^1 ; Rahmawati, Fitria^1 ; Rochman, Refada A.^2 ; Syahputra, Rahmat J. E.^1 ; Prameswari, Arum P.^1

Research Group of Solid State Chemistry and Catalysis, Chemistry Dpartment, Sebelas Maret University, Jl.Ir. Sutami 36 A, Kentingan, Surakarta

57126, Indonesia^1

Chemistry Department, Faculty of Mathematics and Naatural Science, Sebelas Maret University, Jl. Ir. Sutami 36 A, Kentingan Surakarta

57126, Indonesia^2

关键词: Hydrocarbon chains;    La0.6sr0.4co0.2fe0.8o3;    Maximum power density;    Nickel powders;    Screen printing methods;    Single cell performance;    Single cells;    YSZ electrolytes;   

Others  :  https://iopscience.iop.org/article/10.1088/1757-899X/299/1/012087/pdf
DOI  :  10.1088/1757-899X/299/1/012087

学科分类：材料科学（综合）

来源: IOP

【 摘 要 】

This research aims to convert polypropylene plastic to polypropylene oil through pyrolysis method and use the polypropylene oil as fuel for Solid Oxide Fuel Cell, SOFC, to produce electricity. The material for SOFC single cell are Ni-YSZ, YSZ, and LSCF as anode, electrolyte and cathode, respectively. YSZ is yttria-stabilized-zirconia. Meanwhile, LSCF is a commercial La0.6Sr0.4Co0.2Fe0.8O3. The Ni-YSZ is a composite of YSZ with nickel powder. LSCF and Ni-YSZ slurry coated both side of YSZ electrolyte pellet through screen printing method. The result shows that, the produced polypropylene oil consist of C8to C27hydrocarbon chain. Meanwhile, a single cell performance test at 673 K, 773 K and 873 K with polypropylene oil as fuel, found that the maximum power density is 1.729 μW. cm-2at 673 K with open circuit voltage value of 9.378 mV.