Corrosion Behavior of Carbon Steel in Concrete Material Composed of Tin Slag Waste in Aqueous Chloride Solution

International Conference on Chemistry and Material Science 2017

化学;材料科学

Rustandi, Andi^1 ; Cahyadi, Agung^1 ; Siallagan, Sonia Taruli^1 ; Nawawi, Fuad Wafa'^1 ; Pratesa, Yudha^1

Metallurgy and Materials Engineering Department, Faculty of Engineering, Universitas Indonesia, Depok, Indonesia^1

关键词: Chemical compositions;    Corrosion behavior;    Cyclic polarization;    Electrochemical impedance;    Electrochemical test;    Material application;    Ordinary Portland cement;    Sodium chloride solution;   

Others  :  https://iopscience.iop.org/article/10.1088/1757-899X/299/1/012047/pdf
DOI  :  10.1088/1757-899X/299/1/012047

学科分类：材料科学（综合）

来源: IOP

【 摘 要 】

Tin slag is a byproduct of tin ore smelting process which is rarely utilized. The main purpose of this work is to investigate the use of tin slag for concrete cement material application compared to the industrial Ordinary Portland Cement (OPC). Tin slag composition was characterized by XRD and XRF analysis. The characterization results showed the similar chemical composition of tin slag and OPC. It also revealed the semi crystalline structure of tin slag sample. Several electrochemical tests were performed to evaluate corrosion behavior of tin slag, OPC and various mixed composition of both materials and the addition of CaO. The corrosion behavior of OPC and tin slag were evaluated by using Cyclic Polarization, Electrochemical Impedance Spectroscopy (EIS) and Electrochemical Frequency Modulation (EFM) methods. Aqueous sodium chloride (NaCl) solution with 3.5% w.t concentration which similar to seawater was used as the electrolyte in this work. The steel specimen used as the reinforce bar (rebar) material of the concrete was carbon steel AISI 1045. The rebar was embedded in the concrete cement which composed of OPC and the various composition of tin slag including slag without addition of CaO and slag mixed with addition of 50 % CaO. The electrochemical tests results revealed that tin slag affected its corrosion behavior which becoming more active and increasing the corrosion rate as well as decreasing the electrochemical impedance.