Mechanical properties of hybrid SiC/CNT filled toughened epoxy nanocomposite

International Conference on Advances in Manufacturing and Materials Engineering 2017

机械制造;材料科学

Ratim, S.^1,2 ; Ahmad, S.^1 ; Bonnia, N.N.^2 ; Yahaya, Sabrina M.^3

School of Applied Physics, Faculty of Science and Technology, Universiti Kebangsaan Malaysia, Bangi, Selangor

43600, Malaysia^1

Materials Technology Programme, Faculty of Applied Sciences, Universiti Teknologi MARA, Selangor, Shah Alam

40450, Malaysia^2

Department of Applied Chemistry, Faculty of Applied Sciences, Universiti Teknologi MARA, Selangor, Shah Alam

40450, Malaysia^3

关键词: Compression-molding technique;    Epoxidized natural rubber;    Epoxy nanocomposites;    Hybrid nanocomposites;    Hybridization effects;    Mechanical stirring;    Nanocomposite samples;    Ultrasonic cavitation;   

Others  :  https://iopscience.iop.org/article/10.1088/1757-899X/290/1/012005/pdf
DOI  :  10.1088/1757-899X/290/1/012005

学科分类：材料科学（综合）

来源: IOP

【 摘 要 】

Mechanical properties of epoxy nanocomposites filled single filler have been extensively studied by various researchers. However, there are not much discovery on the behavior of hybrid nanocomposite. In this study, single and hybrid nanocomposites of toughened epoxy filled CNT/SiC nanoparticles were investigated. The hybrid nanocomposites samples were prepared by combining CNT and SiC nanoparticles in toughened epoxy matrix via mechanical stirring method assisted with ultrasonic cavitations. Epoxy resin and liquid epoxidized natural rubber (LENR) mixture were first blend prior to the addition of nanofillers. Then, the curing process of the nanocomposite samples were conducted by compression molding technique at 130°C for 2 hours. The purpose of this study is to investigate the hybridization effect of CNT and SiC nanoparticles on mechanical properties toughened epoxy matrix. The total loading of single and hybrid nanofillers were fixed to 4% volume are 0, 4C, 4S, 3S1C, 2S2C, and 1S3C. Mechanical properties of hybrid composites show that the highest value of tensile strength achieved by 3S1C sample at about 7% increment and falls between their single composite values. Meanwhile, the stiffness of the same sample is significantly increased at about 31% of the matrix. On the other hand, a highest flexural property is obtained by 1S3C sample at about 20% increment dominated by CNT content. However, the impact strength shows reduction trend with the addition of SiC and CNT into the matrix. The hybridization of SiC and CNT show highest value in sample 1S3C at about 3.37 kJ/m2of impact energy absorbed. FESEM micrograph have confirmed that better distributions and interaction observed between SiC nanoparticles and matrix compared to CNT, which contributed to higher tensile strength and modulus.