Development of zinc-plated regenerator material

Cryogenic Engineering Conference 2017

材料科学;物理学

Xu, M.Y.^1 ; Morie, T.^1 ; Tsuchiya, A.^1

Technology Research Center, Sumitomo Heavy Industries, Ltd., 2-1-1 Yato-cho, Nishitokyo-city, Tokyo

188-8585, Japan^1

关键词: Bronze screens;    Comparison test;    Cooling Capacity;    Cooling performance;    G-m cryocooler;    Low temperatures;    Regenerator materials;    Temperature decrease;   

Others  :  https://iopscience.iop.org/article/10.1088/1757-899X/278/1/012167/pdf
DOI  :  10.1088/1757-899X/278/1/012167

学科分类：材料科学（综合）

来源: IOP

【 摘 要 】

An effective way to improve the efficiency of a cryocooler is to improve the efficiency of the regenerator. In general, the heat capacity of materials decreases as temperature decreases. Thus, when temperature is below 40 K, lead or bismuth spheres are often used as regenerator materials. However, the pressure drop in a sphere regenerator is much larger than that in a screen regenerator. To overcome this dilemma, Xu et al. reported that cooling performance at the temperature of less than 40 K was improved when using tin-plated screens at the cold end of the regenerator. However, the reliability of tin at low temperatures is still not verified fully because of its phase transition from a normal β phase to an abnormal α phase, which may result in a significant reduction of the mechanical strength. In this paper, a zinc-plated screen is proposed as another potential alternative. A comparison test was performed with a two-stage GM cryocooler by replacing part of the first stage regenerator material, phosphorus bronze screens, with zinc-plated screens. Compared to a regenerator filled with bronze screens, the cooling capacity of the first stage increased by about 11% at 40 K and 60% at 30 K with these zinc-plated screens. The detailed experimental results are reported in this paper.