Preparation of poly (arylene ether nitrile)/NzdFeB composite film with excellent thermal properties and tensile strength

1st International Conference on Frontiers of Materials Synthesis and Processing

材料科学;化学

Pan, Hai^1 ; Xu, Mingzhen^1 ; Liu, Xiaobo^1

Centre for Applied Chemistry, High Temperature Resistant Polymers and Composites, Key Laboratory of Sichuan Province, University of Electronic Science and Technology, Chengdu, China^1

关键词: Decomposition temperature;    Fracture morphology;    Poly(arylene ether nitrile);    SEM analysis;    Solution-casting method;    Universal testing machines;    Weight loss;    Well-dispersed;   

Others  :  https://iopscience.iop.org/article/10.1088/1757-899X/274/1/012089/pdf
DOI  :  10.1088/1757-899X/274/1/012089

学科分类：材料科学（综合）

来源: IOP

【 摘 要 】

PEN/NdFeB composite films were prepared by the solution casting method. The thermal properties, fracture morphology and tensile strength of the composite films were tested by DSC, TGA, SEM and electromechanical universal testing machine, respectively. The results reveal that the composite film has good thermal properties and tensile strength. Glass-transition temperature and decomposition temperatures at weight loss of 5% ot the composite films retain at 166±1 C and 462±4 C, respectively. The composite film with 5 wt.% NdFeB has the best tensile strength value for 100.5 MPa. In addition, it was found that the NdFeB filler was well dispersed in PEN matrix by SEM analysis.