Corrosion behaviour of Al-Fe-Ti-V medium entropy alloy

4th International Conference on Mechanical, Materials and Manufacturing

材料科学;机械制造

Bodunrin, M.O.^1,2 ; Obadele, B.A.^3 ; Chown, L.H.^2 ; Olubambi, P.A.^3

Department of Metallurgical and Materials Engineering, Federal University of Technology Akure, PMB 704, Ondo State, Nigeria^1

School of Chemical and Metallurgical Engineering, University of Witwatersrand, Johannesburg

2050, South Africa^2

Centre for Nanoengineering and Tribocorrosion, School of Mining, Metallurgy and Chemical Engineering, University of Johannesburg, Doornfontein Campus, Johannesburg, South Africa^3

关键词: Body-centered cubic;    Corrosion behaviour;    Corrosion performance;    Corrosive solution;    Engineering applications;    Face centered cubic structure;    Open circuit potential;    Superior corrosion;   

Others  :  https://iopscience.iop.org/article/10.1088/1757-899X/272/1/012028/pdf
DOI  :  10.1088/1757-899X/272/1/012028

学科分类：材料科学（综合）

来源: IOP

【 摘 要 】

Alloys containing up to four multi-principal elements in equiatomic ratios are referred to as medium entropy alloys (MEA). These alloys have attracted the interest of many researchers due to the superior mechanical properties it offers over the traditional alloys. The design approach of MEA often results to simple solid solution with either body centered cubic; face centered cubic structures or both. As the consideration for introducing the alloys into several engineering application increases, there have been efforts to study the corrosion behaviour of these alloys. Previous reports have shown that some of these alloys are more susceptible to corrosion when compared with traditional alloys due to lack of protective passive film. In this research, we have developed AlFeTiV medium entropy alloys containing two elements (Ti and Al) that readily passivate when exposed to corrosive solutions. The alloys were produced in vacuum arc furnace purged with high purity argon. Open circuit potential and potentiodynamic polarisation tests were used to evaluate the corrosion behaviour of the as-cast AlFeTiV alloy in 3.5 wt% NaCl and 1 M H2SO4. The corrosion performance of the alloy was compared with Ti-6Al-4V alloy tested under similar conditions. The results show that unlike in Ti-6Al-4V alloy, the open circuit potential of the AlFeTiV alloy move towards the negative values in both 3.5 wt% NaCl and 1 M H2SO4solutions indicating that self-activation occurred rapidly on immersion. Anodic polarisation of the alloys showed that AlFeTiV alloy exhibited a narrow range of passivity in both solutions. In addition, the alloys exhibited lower Ecorr and higher Icorr when compared with traditional Ti-6Al-4V alloy. The traditional Ti-6Al-4V alloy showed superior corrosion resistant to the AlFeTiV alloy in both 3.5 wt.% NaCl and 1 M H2SO4solutions.