Development of references of anomalies detection on P91 material using Self-Magnetic Leakage Field (SMLF) technique

4th International Conference on Mechanical Engineering Research

Husin, Shuib^1 ; Pauzi, Ahmad Afiq^1 ; Yunus, Salmi Mohd^1 ; Ghafar, Mohd Hafiz Abdul^1 ; Sekari, Saiful Adilin^1

Material Engineering Group, TNB Research, Malaysia^1

关键词: Anomalies detections;    Boiler components;    Inspection tests;    Internal defects;    Non-destructive technique;    Non-destructive test;    Self-magnetic leakage field;    Surface preparation;   

Others  :  https://iopscience.iop.org/article/10.1088/1757-899X/257/1/012064/pdf
DOI  :  10.1088/1757-899X/257/1/012064

来源: IOP

【 摘 要 】

This technical paper demonstrates the successful of the application of self-magnetic leakage field (SMLF) technique in detecting anomalies in weldment of a thick P91 materials joint (1 inch thickness). Boiler components such as boiler tubes, stub boiler at penthouse and energy piping such as hot reheat pipe (HRP) and H-balance energy piping to turbine are made of P91 material. P91 is ferromagnetic material, therefore the technique of self-magnetic leakage field (SMLF) is applicable for P91 in detecting anomalies within material (internal defects). The technique is categorized under non-destructive technique (NDT). It is the second passive method after acoustic emission (AE), at which the information on structures radiation (magnetic field and energy waves) is used. The measured magnetic leakage field of a product or component is a magnetic leakage field occurring on the component's surface in the zone of dislocation stable slipbands under the influence of operational (in-service) or residual stresses or in zones of maximum inhomogeneity of metal structure in new products or components. Inter-granular and trans-granular cracks, inclusion, void, cavity and corrosion are considered types of inhomogeneity and discontinuity in material where obviously the output of magnetic leakage field will be shown when using this technique. The technique does not required surface preparation for the component to be inspected. This technique is contact-type inspection, which means the sensor has to touch or in-contact to the component's surface during inspection. The results of application of SMLF technique on the developed P91 reference blocks have demonstrated that the technique is practical to be used for anomaly inspection and detection as well as identification of anomalies' location. The evaluation of this passive self-magnetic leakage field (SMLF) technique has been verified by other conventional non-destructive tests (NDTs) on the reference blocks where simulated defects/anomalies have been developed inside at the weldment. The results from the inspection test showed that the signatures of magnetic leakage field gradient distribution prove that the peak is found on the location of defect/anomaly in the reference block. It is in agreement with the evidence of anomaly that seen in the radiography test film (RT).