Effect of Sintering Temperature on the Microstructure and Mechanical Properties of Low-Cost Light-Weight Proppant Ceramics
材料科学;物理学
Wang, K.Y.^1 ; Wang, H.J.^1 ; Zhou, Y.^1 ; Wu, Y.Q.^1 ; Li, G.M.^1 ; Tian, Y.M.^2
School of Materials Science and Engineering, Taiyuan University of Science and Technology, Taiyuan
030024, China^1
Shanxi Engineering Vocational College, Taiyuan
030009, China^2
关键词: Apparent porosity;    Bulk density;    Coal gangues;    Light weight;    Low costs;    Microstructure and mechanical properties;    Proppant;    Sintering temperatures;   
Others  :  https://iopscience.iop.org/article/10.1088/1757-899X/230/1/012022/pdf
DOI  :  10.1088/1757-899X/230/1/012022
学科分类:材料科学(综合)
来源: IOP
PDF
【 摘 要 】

In this paper, the low-cost light-weight proppant ceramics were prepared with the solid wastes of coal gangue as the raw materials, and the effect of sintering temperature on the apparent porosity, bulk density, bending strength, microstructure and phase composition were investigated. The results showed that the ceramics, sintered at 1350°C, has the best performance with the bending strength of 85MPa, bulk density of 2.7 g/cm3 and apparent porosity of 18%. These properties of ceramics were very close to that of the bauxite-sintered, and thus the gangue were very probably selected for the preparation of proppants that involved in the exploitation of coalbed methane.