Fabrication and Properties of Al-Cu-Mg-Zn Series Alloys with Low Hot Cracking Tendency for Liquid Forging

International Conference on Materials Sciences and Nanomaterials

材料科学;物理学

Sun, Y.G.^1 ; Su, Y.N.^1 ; Du, Z.M.^1 ; Chen, L.H.^2 ; Wang, C.S.^2

School of Materials Science and Engineering, Harbin Institute of Technology, Harbin

150001, China^1

Beijing North Vehicle Group Co. Ltd., Beijing

100072, China^2

关键词: 2024 alloy;    Brinell hardness;    Elongation to fracture;    Hot cracking;    Liquid forging;    New alloys;    Properties of Al;    Series alloys;   

Others  :  https://iopscience.iop.org/article/10.1088/1757-899X/230/1/012036/pdf
DOI  :  10.1088/1757-899X/230/1/012036

学科分类：材料科学（综合）

来源: IOP

【 摘 要 】

Twelve new kinds of Al-Cu-Mg-Zn alloys with different components were designed on the basis of optimizing main alloying elements, including Zn, Mg and Cu to resolve hot crack problems of Al-Cu-Mg-Zn series alloys during liquid forging. Hot cracking susceptibility (HCS) was adopted to characterize hot cracking tendency, evaluated using constrained rod casting in a steel mould. The influence of those three main alloying elements on the hot cracking tendency and the mechanical properties of new alloys were researched. The results show that most of those new alloys have better hot crack tendency performances than 2024 alloy and 7075 alloy. The 8th alloy, Al-5Cu-4.5Mg-2.5Zn, shows best mechanical properties after liquid forging, which hot crack tendency index is the lowest, only reaching 40. The tensile strength is 327 MPa and the elongation to fracture is 2.7%, which Brinell hardness reaches 107 N/mm2.