Effect of urea deproteinization on catalytic hydrogenation of natural rubber latex

Innovation in Polymer Science and Technology 2016

材料科学;化学

Cifriadi, A.^1 ; Chalid, M.^2 ; Puspitasari, S.^1

Indonesian Rubber Research Institute, Jl. Salak No 1, Bogor, West Java

16151, Indonesia^1

Departement of Metallurgy and Materials, Faculty of Engineering, University of Indonesia, Kampus UI Depok, Depok, West-Java

16424, Indonesia^2

关键词: Catalytic hydrogenation;    Deproteinization;    Deproteinized natural rubber latices;    Hydrazine hydrate;    Natural rubber latex;    Oxidative properties;    Protein contents;    Sodium dodecyl sulphate;   

Others  :  https://iopscience.iop.org/article/10.1088/1757-899X/223/1/012010/pdf
DOI  :  10.1088/1757-899X/223/1/012010

学科分类：材料科学（综合）

来源: IOP

【 摘 要 】

Natural rubber is unsaturated biopolymer which has low resistance to heat, oxygen, and ozone. Chemical modification of natural rubber by catalytic hydrogenation can improve its oxidative property. In this study, the catalytic hydrogenation of natural rubber was investigated in latex phase after reduction of protein content with urea. Hydrogenation of deproteinized natural rubber latex was performed by using diimide which generated insitu from hydrazine hydrate/hydrogen peroxide and catalyst (boric acid, cupric sulfate and cupric acetate) at 70°C for 5 h. The hydrogenation system was stabilized with sodium dodecyl sulphate. The hydrogenation of deproteinized natural rubber (HDPNR) was confirmed by FTIR analysis. The result indicated that cupric sulphate was extremely active catalyst which was showed by the elimination of C=C transmittance bands at 1660 cm-1on HDPNR spectra and highest degree of hydrogenation. Furthermore, urea deproteinization increased possibility of side reactions during catalytic hydrogenation as seen on the reduction of gel content compared to undeproteinized natural rubber.