Synthesis and Characterization of Hybrid CF/MWCNTS/Epoxy Resin Composite System

2nd International Conference on Design, Materials, and Manufacturing

材料科学;机械制造

Fouda, Hany^1 ; Guo, Lin^1 ; Yue, Yonghai^1 ; Chen, Ke^1 ; Elsharkawy, Karim^1

School of Chemistry and Environment, Beijing University of Aeronautics and Astronautics, Beijing, China^1

关键词: Composite samples;    Epoxy resin system;    Fiber reinforced polymer composites;    Interface bonding;    Interface modification;    Matrix modification;    Reinforcing fibers;    Synthesis and characterizations;   

Others  :  https://iopscience.iop.org/article/10.1088/1757-899X/220/1/012021/pdf
DOI  :  10.1088/1757-899X/220/1/012021

学科分类：材料科学（综合）

来源: IOP

【 摘 要 】

In the present investigation, two methods were used for addition multiwall carbon nanotubes (MWCNTS) into carbon fiber (CF)/epoxy resin composite system. The mechanical properties of the prepared samples were compared to show the best method for addition of MWCNTSfrom point of view of mechanical properties. The introduction of carbon nanotubes (CNTs) into fiber reinforced polymer composites has been achieved mainly via two routes: mixing CNTs entirely throughout the matrix (matrix modification) or attaching CNTs onto reinforcing fibers (interface modification). In all previous references the addition of CNTs occur through one route from the two routes but in this research, we introduced MWCNTSinto CF/epoxy resin composite through the two routes at the same time. Three CF composite samples were prepared CF/epoxy resin composite (C1), CF/1wt% MWCNTS/epoxy resin composite (C2) in which MWCNTSadded via one route (epoxy resin system) and the third sample was CF/1wt% MWCNTS/ epoxy resin composite (C3) in which MWCNTSadded via two routes (epoxy resin and CF fabric). The result shows that the mechanical properties of C3>C2>C1, for example, the flexural strength of C3 higher than C2 by 19% and C2 higher than C1 by 51% respectively. This is because addition MWCNTSvia two routes increase the ability of good mixing of CNTSwith epoxy resin and good dispersion of CNTs into the CF fabric surface and this leads to improve the interface bonding between the CF and epoxy so improve the mechanical properties.