Performance of solvent-borne intumescent fire protective coating with Palm oil clinker as novel bio-filler on steel

International Technical Postgraduate Conference

Mustapa, S.A.S.^1 ; Ramli Sulong, N.H.^1

Department of Civil Engineering, Faculty of Engineering, University of Malaya, Lembah Pantai, Kuala Lumpur

50603, Malaysia^1

关键词: Acrylic binders;    Field emission scanning electron microscopy;    High thermal stability;    Intumescent coating;    Metal surfaces;    Palm oil clinkers;    Protection performance;    Water-resistances;   

Others  :  https://iopscience.iop.org/article/10.1088/1757-899X/210/1/012027/pdf
DOI  :  10.1088/1757-899X/210/1/012027

来源: IOP

【 摘 要 】

This research deals with contribution of hybrid fillers with palm oil clinker (POC) as a novel bio-filler in solvent-borne intumescent fire protective coating for steel. The hybrid fillers with POC were mixed in appropriate amount of additives and acrylic binder to produce the intumescent coatings. The intumescent coatings were characterized by using Bunsen burner test, surface spread of flame, thermogravimetric analysis, field emission scanning electron microscopy, static immersion and Instron micro tester equipment. Specimen with POC as a single filler has significantly enhanced the fire protection performances of the intumescent coating due to the high thermal stability of POC, where less than 10% of temperature different when compared to specimens with hybrid fillers. From the flame spread classification, class 1 is the best classification while Class 4 is the worst and considered high risk. All specimens was classified as class 1 since the final spread of flame was less than 165 mm. For hybrid fillers composition, specimen consist of POC/Al(OH)3/TiO2has significantly improved the water resistance of the coating due to the low solubility of Al(OH)3in water, while specimen contain of Mg(OH)2had higher mechanical strength due to the strong bonding between the metal surface and acrylic binder/Mg(OH)2filler. It was found that coating with the incorporation of all hybrid fillers gives excellent fire protection performance with good thermal stability, water resistance and mechanical properties. It can be concluded that, the selection of appropriate composition of fillers and binder in intumescent coating was highly influence the intumescent coating performance.