Technique Incorporating Cooling & Contraction / Expansion Analysis to Illustrate Shrinkage Tendency in Cast Irons

International Conference on Innovative Research - ICIR Euroinvent 2017

Stan, S.^1 ; Chisamera, M.^1 ; Riposan, I.^1 ; Neacsu, L.^1 ; Cojocaru, A.M.^1 ; Stan, I.^1

Materials Processing and Ecometallurgy, Politehnica University of Bucharest, 313, Independentei Spl., 6th District, Bucharest

060042, Romania^1

关键词: Cast iron quality;    Equilibrium temperatures;    Experimental devices;    First derivative;    Initial expansions;    ITS applications;    Metastable equilibria;    Solidification sequence;   

Others  :  https://iopscience.iop.org/article/10.1088/1757-899X/209/1/012017/pdf
DOI  :  10.1088/1757-899X/209/1/012017

来源: IOP

【 摘 要 】

With the more widespread adoption of thermal analysis testing, thermal analysis data have become an indicator of cast iron quality. The cooling curve and its first derivative display patterns that can be used to predict the characteristics of a cast iron. An experimental device was developed with a technique to simultaneously evaluate cooling curves and expansion or contraction of cast metals during solidification. Its application is illustrated with results on shrinkage tendency of ductile iron treated with FeSiMgRECa master alloy and inoculated with FeSi based alloys, as affected by mould rigidity (green sand and resin sand moulds). Undercooling at the end of solidification relative to the metastable (carbidic) equilibrium temperature and the expansion within the solidification sequence appear to have a strong influence on the susceptibility to macro - and micro - shrinkage in ductile iron castings. Green sand moulds, as less rigid moulds, encourage the formation of contraction defects, not only because of high initial expansion values, but also because of a higher cooling rate during solidification, and consequently, increased undercooling below the metastable equilibrium temperature up to the end of solidification.