Microstructure and mechanical properties of 980MPa grade Fe-Mn-Al-C lightweight steel

4th International Conference on Advanced Composite Materials and Manufacturing Engineering 2017

材料科学;化学

Jiang, Yinghua^1,2 ; Xie, Chunqian^1,2

Shougang Research Institute of Technology, Beijing

100043, China^1

Beijing Key Laboratory of Green Recyclable Process for Iron and Steel Production Technology, Beijing

100043, China^2

关键词: Annealing process;    Corrosion-resistant;    Light-weight steels;    Microstructure and mechanical properties;    Properties and microstructures;    Strain hardening behavior;    Strength and ductilities;    Strength and elongations;   

Others  :  https://iopscience.iop.org/article/10.1088/1757-899X/207/1/012053/pdf
DOI  :  10.1088/1757-899X/207/1/012053

学科分类：材料科学（综合）

来源: IOP

【 摘 要 】

Fe-Mn-Al-C lightweight high strength steel, adding more Mn, Al and C elements into conventional AHSS, shows amazing mechanical properties, corrosion resistant and weight reduction than conventional AHSS. The mechanical properties and microstructure of Fe-15Mn-6.8Al-0.9C-0.2Ti steel after annealing process were investigated. The results show that the microstructures consisted of secondary phases TiC precipitate and ferrite in the austenite matrix. The tensile strength and elongation of the steel are 985MPa and 36%, respectively. The density is 6.86g/cm3. Continuous strain hardening behavior provides Fe-Mn-Al-C lightweight steel with perfect combination of strength and ductility.