Effect of NiO and Light Intensity on Dielectric Constant of SiO2-B2O3-Bi2O3-Na2CO3 Glass Based on Silica Gel of Natural Sands
Diantoro, M.^1,2 ; Muniroh, Z.^1 ; Zaini, B.^1 ; Mustikasari, A.A.^1 ; Nasikhudin^1,2,3 ; Hidayat, A.^1,2 ; Taufiq, A.^1,2 ; Sunaryono^1,2 ; Mufti, N.^1,2
Department of Physics, Faculty of Mathematics and Natural Sciences, Universitas Negeri Malang, State University of Malang, Jl. Semarang 5, Malang
65145, Indonesia^1
Center for Minerals and Advanced Materials, Faculty of Mathematics and Natural Sciences, Universitas Negeri Malang, State University of Malang, Jl. Semarang 5, Malang
65145, Indonesia^2
Departmet of Physics, Faculty of Mathematics and Natural Sciences, Universitas Gadjah Mada, Indonesia^3
关键词: Glass properties;    Light intensity;    Natural sand;    Processing parameters;    SEM-EDAX;    Silica sol gels;    Weighting process;   
Others  :  https://iopscience.iop.org/article/10.1088/1757-899X/202/1/012056/pdf
DOI  :  10.1088/1757-899X/202/1/012056
来源: IOP
PDF
【 摘 要 】

The use of silica in various fields is significantly increasing. One common application is silica based functional glass which has naturally show specific dielectric, optical, and magnetic properties. Many studies have been performing to explore the influence of dopant, composition, and other processing parameters as well as employing various characterization. In the previous work, we report the use of silica from silica sands. To reduce the melting temperature, we used silica sol-gel beside the utilization of some oxides such as B2O3, Na2CO3, and Bi3O3. We also used NiO as dopant explore the glass properties. We have prepared a series of sample with the composition of 50SiO2-25B2O3-(6.5-x) Bi3O3-18.5Na2CO3-xNiO (x = 0, 1, 2, 3 and 4 wt%). After weighting process, the composition was blended, then heated to 450 °C for 120 minutes and then raised at 950 °C for 60 minutes in the crucible. Then samples of glass separated from the crucible and in the characterization of the structure using the DTA, XRD, SEM-EDAX and FTIR and measuring dielectric constant using a capacitance meter. The increase of NiO dopant resulted in increasing the dielectric constant of glass. On the other hand, the dielectric constant gradually decreases with the increase of light intensity. One can be noted that the applied intensity give rise to the step-like decrease of the dielectric constant. Whereas, the increasing magnetic field indicate the increase of dielectric constant.