Effects of Austenitizing and Forging on Mechanical Properties of MIL A-12560/AISI 4340 Steel
Herbirowo, S.^1 ; Adjiantoro, B.^1 ; Romijarso, T.B.^1
Research Center for Metallurgy and Materials, Indonesian Institute of Science (P2MM-LIPI), Kawasan Puspiptek, Gedung 470, Tangerang Selatan, Indonesia^1
关键词: Austenitizing;    Austenizing temperature;    auztenitizing;    Hardness measurement;    Material strength;    Metallographic observations;    Tempered martensite;    Tempering temperature;   
Others  :  https://iopscience.iop.org/article/10.1088/1757-899X/202/1/012084/pdf
DOI  :  10.1088/1757-899X/202/1/012084
来源: IOP
PDF
【 摘 要 】

Laterite steels might be used for alternative armored steels. Their properties can be improved in various ways, such as by heat treatment. This paper reports the influences of tempering temperature on the hardness and microstructure of the modified MIL A-12560/AISI 4340 steels. Samples were austenitized at 1200, 1000, and 800°C and forged at 100, 75, and 50 tons. Mechanical properties consisted of Hardness measurement was conducted by Brinell indentation and metallographic observation was conducted by scanning electron microscopy (SEM). The results showed that increasing forging force until 100 tons can decrease hardness. The formation of the microstructure consists of tempered martensite containing ferrite and dual phase perlite. The presence of void and porous can also decrease hardness. Decreasing austenizing temperature from 1200 °C to 800°C can increase material strength and hardness.