Investigation on the cold rolling and structuring of cold sprayed copper-coated steel sheets

19th Chemnitz Seminar on Materials Engineering – 19. Werkstofftechnisches Kolloquium

Bobzin, K.^1 ; Öte, M.^1 ; Wiesner, S.^1 ; Gerdt, L.^1 ; Senge, S.^2 ; Hirt, G.^2

Surface Engineering Institute, RWTH Aachen University, Germany^1

Institute of Metal Forming, RWTH Aachen University, Germany^2

关键词: Cold gas spraying;    Cold rolling process;    Heat treated condition;    High pressure die casting;    High pressure die casts;    Lightweight design;    Surface pretreatment;    Thickness reduction;   

Others  :  https://iopscience.iop.org/article/10.1088/1757-899X/181/1/012028/pdf
DOI  :  10.1088/1757-899X/181/1/012028

来源: IOP

【 摘 要 】

A current driving force of research is lightweight design. One of the approaches to reduce the weight of a component without causing an overall stiffness decrease is the use of multi-material components. One of the main challenges of this approach is the low bonding strength between different materials. Focusing on steel-aluminum multi-material components, thermally sprayed copper coatings can come into use as a bonding agent between steel sheets and high pressure die cast aluminum to improve the bonding strength. This paper presents a combination of cold gas spraying of copper coatings and their subsequent structuring by rolling as surface pretreatment method of the steel inserts. Therefore, flat rolling experiments are performed with samples in "as sprayed" and heat treated conditions to determine the influence of the rolling process on the bond strength and the formability of the coating. Furthermore, the influence of the rolling on the roughness and the hardness of the coating was examined. In the next step, the coated surface was structured, to create a surface topology suited for a form closure connection in a subsequent high-pressure die casting process. No cracks were observed after the cold rolling process with a thickness reduction of up to= 14 % for heat treated samples. Structuring of heat treated samples could be realized without delamination and cracking.