Evaluation of in-situ deformation experiments of TRIP steel | |
Procházka, J.^1 ; Kuerová, L.^1 ; Bystrianský, M.^1 | |
RTI, UWB in Pilsen, Universitni 8, Pilsen, EU | |
30614, Czech Republic^1 | |
关键词: Annealing temperatures; Chemical compositions; Deformation stages; Electron backscattering diffraction; In-situ tensile testing; Reference material; Situ deformation; Transformation induced plasticity; | |
Others : https://iopscience.iop.org/article/10.1088/1757-899X/179/1/012059/pdf DOI : 10.1088/1757-899X/179/1/012059 |
|
来源: IOP | |
![]() |
【 摘 要 】
The paper reports on the behaviour of low alloyed TRIP (transformation induced plasticity) steel with Niobium during tensile test. The structures were analysed using in-situ tensile testing coupled with electron backscattering diffraction (EBSD) analysis carried out in scanning electron microscope (SEM). Steel specimens were of same chemical composition; however three different annealing temperatures, 800 C, 850 C and 950 C, were applied to the material during the heat treatment. The treatment consisted of annealing for 20 minutes in the furnace; cooling in salt bath after the heating and holding at 425 C for 20 minutes for all the samples. Untreated bar was used as reference material. Flat samples for deformation stage were cut out of the heat-treated bars. In situ documentation of microstructure and crystallography development were carried out during the deformation experiments. High deformation lead to significant degradation of EBSD signal.【 预 览 】