Residual stresses in shape memory alloy fiber reinforced aluminium matrix composite

Colloquium of Advanced Mechanics 2016

Loong, Tang Tsz^1 ; Jamian, Saifulnizan^2 ; Ismail, Al Emran^2 ; Muhd Nur, Nik Hisyammudin^1 ; Watanabe, Yoshimi^3

Faculty of Mechanical and Manufacturing Engineering, Universiti Tun Hussein Onn Malaysia, Johor, Malaysia^1

Crashworthiness and Collisions Research Group, Faculty of Mechanical and Manufacturing Engineering, Universiti Tun Hussein Onn Malaysia, Johor, Malaysia^2

Department of Mechanical Engineering, Nagoya Institute of Technology, Nagoya, Japan^3

关键词: Aluminium matrix composites;    Compressive residual stress;    Distribution of residual stress;    Heating and cooling;    Loading and unloading;    Manufacturing process;    Shape memory alloy fibers;    Thermal coefficients;   

Others  :  https://iopscience.iop.org/article/10.1088/1757-899X/165/1/012002/pdf
DOI  :  10.1088/1757-899X/165/1/012002

来源: IOP

【 摘 要 】

Process-induced residual stress in shape memory alloy (SMA) fiber reinforced aluminum (Al) matrix composite was simulated by ANSYS APDL. The manufacturing process of the composite named as NiTi/Al is start with loading and unloading process of nickel titanium (NiTi) wire as SMA to generate a residual plastic strain. Then, this plastic deformed NiTi wire would be embedded into Al to become a composite. Lastly, the composite is heated form 289 K to 363 K and then cooled back to 300 K. Residual stress is generated in composite because of shape memory effect of NiTi and mismatch of thermal coefficient between NiTi wire and Al matrix of composite. ANSYS APDL has been used to simulate the distribution of residual stress and strain in this process. A sensitivity test has been done to determine the optimum number of nodes and elements used. Hence, the number of nodes and elements used are 15680 and 13680, respectively. Furthermore, the distribution of residual stress and strain of nickel fiber reinforced aluminium matrix composite (Ni/Al) and titanium fiber reinforced aluminium matrix composite (Ti/Al) under same simulation process also has been simulated by ANSYS APDL as comparison to NiTi/Al. The simulation results show that compressive residual stress is generated on Al matrix of Ni/Al, Ti/Al and NiTi/Al during heating and cooling process. Besides that, they also have similar trend of residual stress distribution but difference in term of value. For Ni/Al and Ti/Al, they are 0.4% difference on their maximum compressive residual stress at 363K. At same circumstance, NiTi/Al has higher residual stress value which is about 425% higher than Ni/Al and Ti/Al composite. This implies that shape memory effect of NiTi fiber reinforced in composite able to generated higher compressive residual stress in Al matrix, hence able to enhance tensile property of the composite.