Effect Of Temperature Variation On Wear Behaviour Of Austenitic Stainless Steel

International Engineering Research and Innovation Symposium

Alias, S.K.^1 ; Ahmad, S.^1 ; Abdullah, B.^1 ; Pahroraji, H.F.^1 ; Hamami, G.^1

Faculty of Mechanical Engineering, Universiti Teknologi MARA, Masai, Johor

81750, Malaysia^1

关键词: Abrasion wear;    Effect of temperature;    Pin-on-disk tests;    Resistance properties;    Standard samples;    Surface characterization;    Vickers microhardness tester;    Wear behaviours;   

Others  :  https://iopscience.iop.org/article/10.1088/1757-899X/160/1/012026/pdf
DOI  :  10.1088/1757-899X/160/1/012026

来源: IOP

【 摘 要 】

The effects of boronizing temperatures on the wear and hardness properties of austenitic stainless steel were investigated in this study. The samples were prepared in accordance to standard samples preparation for wear and hardness test. Pack boronizing were conducted using EKabor®1 powder medium at two different temperatures which are 850°C and 950°C. The wear resistance properties were evaluated though pin on disk test and the surface characterization was analyzed through scanning electron microscopy (SEM), observation. Vickers microhardness tester was performed to obtain the hardness of the samples. The results indicated that there are presences of FeB and Fe2B phases on both samples, but thicker FeB phase was produced at Po-950 samples. This resulted in reduction of abrasion wear properties but major improvement of the hardness properties of boronized stainless steel.