Tailored boron steel sheet component properties by selective laser heat treatment

IDDRG2016 conference on "Challenges in Forming High-Strength Sheets".

Asnafi, N.^1,2 ; Andersson, R.^3 ; Persson, M.^4 ; Liljengren, M.^5

VA Automotive, Box 34, Hässleholm

SE-281 21, Sweden^1

School of Science and Technology, Örebro University, Örebro

SE-701 82, Sweden^2

Duroc Special Steel, Luleå

SE-971 88, Sweden^3

Duroc Laser Coating, Luleå

SE-971 88, Sweden^4

Industrial Development Center, Vällaregatan 30, Olofström

SE-293 38, Sweden^5

关键词: Boron steel sheets;    Boron steels;    Hardening depth;    Hardness values;    Hydraulic press;    Laser processing parameters;    Sheet material;   

Others  :  https://iopscience.iop.org/article/10.1088/1757-899X/159/1/012023/pdf
DOI  :  10.1088/1757-899X/159/1/012023

来源: IOP

【 摘 要 】

This investigation is focused on the stamping behaviour of boron steel, the properties of which are modified by selective laser heat treatment. Both CO2and fibre lasers are tested. By using different laser processing parameters, the hardening depth in the 1 mm thick boron steel sheet Boloc 02 is varied. Four routes are tested and verified. The forming operation (in which a so-called flexrail beam is produced) in all four routes is conducted at ambient (room) temperature. The Reference route comprises stamping of the sheet. The GridBlank route starts with selective laser heat treatment of the blank, after which the blank is allowed to cool down, moved to a hydraulic press and stamped. In the GridTube route, the blank is first stamped, after which the part is moved to a laser cell and selectively laser heat treated. The fourth route, the RapidLaser route, is similar to the GridBlank route, but a higher laser speed is used to promote higher total productivity. The GridBlank route results in the highest hardness values and the best shape accuracy. The initial sheet material exhibits a hardness of 200 HV, while the parts produced in the GridBlank route exhibit a hardness of 700 HV.