Press-hardening of zinc coated steel - characterization of a new material for a new process

IDDRG2016 conference on "Challenges in Forming High-Strength Sheets".

Kurz, T.^1 ; Larour, P.^1 ; Lackner, J.^1 ; Steck, T.^1 ; Jesner, G.^2

Voestalpine Stahl GmbH, Research and Development - CTE, Business Unit Coil, voestalpine-Straße 3, Linz

4020, Austria^1

BÖHLER Edelstahl GmbH and Co KG, Tooling - ETT, Mariazeller Strasse 25, Kapfenberg

8605, Austria^2

关键词: Accurate prediction;    Bending properties;    Fracture elongation;    Liquid metal embrittlement;    Lower temperatures;    Modified materials;    Transformation behavior;    Zinc-coated steel;   

Others  :  https://iopscience.iop.org/article/10.1088/1757-899X/159/1/012025/pdf
DOI  :  10.1088/1757-899X/159/1/012025

来源: IOP

【 摘 要 】

Press-hardening of zinc-coated PHS has been limited to the indirect process until a pre-cooling step was introduced before the hot forming to prevent liquid metal embrittlement. Even though that's only a minor change in the process itself it does not only eliminate LME, but increases also the demands on the base material especially in terms of hardenability or phase transformations at temperatures below 700 °C in general. This paper deals with the characterization of a modified zinc-coated material for press-hardening with pre-cooling that assures a robust process. The pre-cooling step itself and especially the transfer of the blank in the hot-forming die is more demanding than the standard 22MnB5 can stand to ensure full hardenability. Therefore the transformation behavior of the modified material is shown in CCT and TTT diagrams. Of the same importance are the changed hot forming temperature and flow curves for material at lower temperatures than typically used in direct hot forming. The resulting mechanical properties after hardening from tensile testing and bending tests are shown in detail. Finally some results from side impact crash tests and correlations of the findings with mechanical properties such as fracture elongation, tensile strength, VDA238 bending angle at maximum force as well as postuniform bending slope are given as well. Fracture elongation is shown to be of little help for damage prediction in side impact crash. Tensile strength and VDA bending properties enable however some accurate prediction of the PHS final damage behavior in bending dominated side impact load case.