A Study on Effect of Graphite Particles on Tensile, Hardness and Machinability of Aluminium 8011 Matrix Material

International Conference on Advances in Materials and Manufacturing Applications 2016

Shankar, B. Latha^1 ; Anil, K.C.^1 ; Karabasappagol, Prasann J.^1

Dept. of Industrial Engineering and Management, Siddaganga Institute of Technology, Karnataka, Tumakuru

572103, India^1

关键词: Aluminium alloy matrix composites;    Aluminium matrix composites;    Engineering properties;    Graphite particles;    Stir casting;    Stir casting method;    Tensile;    Uniform dispersions;   

Others  :  https://iopscience.iop.org/article/10.1088/1757-899X/149/1/012060/pdf
DOI  :  10.1088/1757-899X/149/1/012060

来源: IOP

【 摘 要 】

Industrial application point of view, metal matrix composites in general and Aluminium alloy matrix composites in particular are ideal candidates because of their favourable engineering properties. Being lightweight Aluminium matrix composites are widely used in aircraft, defence and automotive industries. In this work Aluminium 8011 metal matrix was reinforced with fine Graphite particles of 50 μm. developed by two-step Stir casting method. Graphite weight %was varied in the range 2, 4, 6 and 8%. Uniform dispersion of graphite particle is examined under optical microscope. Tensile test coupons were prepared as per standard to determine % of elongation and tensile strength for various % of graphite particle. Hardness of developed composite for various % of graphite particle and Machinability parameters were also studied for effect on surface finish. It was observed that with increase of weight percentage of Graphite particles up to 8% in Aluminium 8011 alloy matrix there was increase in tensile strength, decrease in % of elongation with increase in hardness. Machinability study revealed that, there was decrease in surface roughness with increase in Graphite content.