Fabrication and evaluation of mechanical properties of alkaline treated sisal/hemp fiber reinforced hybrid composite

International Conference on Advances in Materials and Manufacturing Applications 2016

Venkatesha Gupta, N.S.^1 ; Akash^1 ; Sreenivasa Rao, K.V.^1 ; Arun Kumar, D.S.^1

Department of Mechanical Engineering, Siddaganga Institute of Technology, Tumkur, Karnataka

572103, India^1

关键词: Fiber reinforced polymer composites;    Fractured surfaces;    Hybrid composites;    Interfacial characteristics;    Internal structure;    Polymer composite;    Specific strength;    Strength to weight ratio;   

Others  :  https://iopscience.iop.org/article/10.1088/1757-899X/149/1/012093/pdf
DOI  :  10.1088/1757-899X/149/1/012093

来源: IOP

【 摘 要 】

Fiber reinforced polymer composite have acquired a dominant place in variety of applications because of higher specific strength and modulus, the plant based natural fiber are partially replacing currently used synthetic fiber as reinforcement for polymer composites. In this research work going to develop a new material which posses a strength to weight ratio that for exceed any of the present material. The hybrid composite sisal/hemp reinforced with epoxy matrix has been developed by compression moulding technique according to ASTM standards. Sodium hydroxide (NAOH) was used as alkali for treating the fibers. The amount of reinforcement was varied from 10% to 50% in steps of 10%. Prepared specimens were examined for mechanical properties such as tensile strength, flexural strength, and hardness. Hybrid composite with 40wt% sisal/hemp fiber were found to posses higher strength (tensile strength = 53.13Mpa and flexural strength = 82.07Mpa) among the fabricated hybrid composite specimens. Hardness value increases with increasing the fiber volume. Morphological examinations are carried out to analyze the interfacial characteristics, internal structure and fractured surfaces by using scanning electron microscope.