Occurrence of two-stage hardening in C-Mn steel wire rods containing pearlitic microstructure

International Conference on Advances in Materials and Manufacturing Applications 2016

Singh, Balbir^1 ; Sahoo, Gadadhar^1 ; Saxena, Atul^1

Steel Authority of India Limited, R and D Centre for Iron and Steel, Ranchi, Jharkhand, India^1

关键词: Hardening coefficient;    Hot-rolled;    Pearlitic microstructure;    Polygonal ferrites;    Prior austenite grain boundaries;    Reduction in area;    Strain values;    Total elongations;   

Others  :  https://iopscience.iop.org/article/10.1088/1757-899X/149/1/012066/pdf
DOI  :  10.1088/1757-899X/149/1/012066

来源: IOP

【 摘 要 】

The 8 and 10 mm diameter wire rods intended for use as concrete reinforcement were produced/ hot rolled from C-Mn steel chemistry containing various elements within the range of C:0.55-0.65, Mn:0.85-1.50, Si:0.05-0.09, S:0.04 max, P:0.04 max and N:0.006 max wt%. Depending upon the C and Mn contents the product attained pearlitic microstructure in the range of 85-93% with balance amount of polygonal ferrite transformed at prior austenite grain boundaries. The pearlitic microstructure in the wire rods helped in achieving yield strength, tensile strength, total elongation and reduction in area values within the range of 422-515 MPa, 790-950 MPa, 22-15% and 45-35%, respectively. On analyzing the tensile results it was revealed that the material experienced hardening in two stages separable by a knee strain value of about 0.05. The occurrence of two stage hardening thus in the steel with hardening coefficients of 0.26 and 0.09 could be demonstrated with the help of derived relationships existed between flow stress and the strain.