Investigation of corrosion of welded joints of austenitic and duplex stainless steels

4th ModTech International Conference - Modern Technologies in Industrial Engineering

Topolska, S.^1

Silesian University of Technology, Faculty of Mechanical Engineering, Institute of Engineering Materials and Biomaterials, Konarskiego 18A, Gliwice

44-100, Poland^1

关键词: 316 L stainless steel;    Aggressive environment;    Corrosion environments;    Corrosion process;    Duplex stainless steel;    Electrochemical investigations;    Functional properties;    Potentiodynamic tests;   

Others  :  https://iopscience.iop.org/article/10.1088/1757-899X/145/7/072014/pdf
DOI  :  10.1088/1757-899X/145/7/072014

来源: IOP

【 摘 要 】

Investigation of corrosion resistance of materials is one of the most important tests that allow determining their functional properties. Among these tests the special group consist electrochemical investigations, which let to accelerate the course of the process. These investigations allow rapidly estimating corrosion processes occurring in metal elements under the influence of the analysed environment. In the paper are presented results of investigations of the resistance to pitting corrosion of the steel of next grades: austenitic 316L and duplex 2205. It was also analysed the corrosion resistance of welded joints of these grades of steel. The investigations were conducted in two different corrosion environments: in the neutral one (3.5 % sodium chloride) and in the aggressive one (0.1 M sulphuric acid VI). The obtained results indicate different resistance of analysed grades of steel and their welded joints in relation to the corrosion environment. The austenitic 316L steel characterizes by the higher resistance to the pitting corrosion in the aggressive environment then the duplex 2205 steel. In the paper are presented results of potentiodynamic tests. They showed that all the specimens are less resistant to pitting corrosion in the environment of sulphuric acid (VI) than in the sodium chloride one. The 2205 steel has higher corrosion resistance than the 316L stainless steel in 3.5% NaCl. On the other hand, in 0.1 M H2SO4, the 316L steel has a higher corrosion resistance than the 2205 one. The weld has a similar, very good resistance to pitting corrosion like both steels.