Study of fatigue behavior of longitudinal welded pipes

4th ModTech International Conference - Modern Technologies in Industrial Engineering

Simion, P.^1 ; Dia, V.^1 ; Istrate, B.^1 ; Hrituleac, G.^1 ; Hrituleac, I.^1 ; Munteanu, C.^2

ArcelorMittal Tubular Products Iasi S.A., Chisinaului street, No 132, Iasi, Romania^1

Gheorghe Asachi Technical University of Iasi-Romania, Faculty of Mechanical Engineering, Blvd. Mangeron, No. 43, Iasi

700050, Romania^2

关键词: Electric-welded pipes;    Fatigue behaviour;    High frequency HF;    Longitudinal welded pipe;    Microstructural analysis;    Normal operations;    Pressure fluctuation;    Real operating conditions;   

Others  :  https://iopscience.iop.org/article/10.1088/1757-899X/145/2/022032/pdf
DOI  :  10.1088/1757-899X/145/2/022032

来源: IOP

【 摘 要 】

During transport and storage of the various fluids, welded pipes are subjected to cyclic loading due to pressure fluctuations that often exceed the prescribed values for normal operation. These cyclic loading can significantly reduce the life of the pipes; as a result the design should be based on the fatigue strength not only on static resistance. In general the fatigue strength of pipes is dependent by strength, pipe geometry and surface quality. In case of the electric longitudinal welded pipes, the fatigue strength is significantly limited by concentration of residual stress and the size of existing defects in the weld seam. This paper presents the fatigue behaviour of the electric welded pipes by high frequency, under conditions that simulate real operating conditions pipes. Fatigue testing was performed on welded pipes made of micro alloyed carbon steels. Some of these pipes were previously subjected to a heat treatment of normalization, in order to also determine the influence of heat treatment on the fatigue strength of welded pipes. To determine and correlate the different factors affecting the fatigue strength, welded pipes were also subjected to various tests: tensile tests, impact tests, measurement of micro hardness, microstructural analysis by optical microscopy and scanning electron microscopy.