Iron atoms redistribution in oxide films of Zr-Fe, Zr-Fe-Cu alloys during corrosion in autoclave at 350°C

10th International School-Conference on Materials for Extreme Environment: Development, Production and Application

Filippov, V.^1 ; Bateev, A.^1

National Research Nuclear University MEPhI, Moscow Engineering Physics Institute, Kashirskoe shosse 31, Moscow

115409, Russia^1

关键词: Alloy compositions;    Corrosion tests;    Fe-Cu alloys;    Growth process;    Iron atoms;    Metallic iron;    Phase distortions;    Water environments;   

Others  :  https://iopscience.iop.org/article/10.1088/1757-899X/130/1/012015/pdf
DOI  :  10.1088/1757-899X/130/1/012015

来源: IOP

【 摘 要 】

The data on changes of iron atoms state in the oxide films of binary Zr-1.24 mas.%Fe and ternary Zr-1.39 mas.%Fe-0.60 mas.%Cu zirconium alloys are obtained. Alloys are subjected to corrosion tests under autoclave conditions at 350°C temperature in a steam-water environment under pressure p = 16.8 MPa. In initial specimens of the alloys the iron atoms are in the form of intermetallic compounds. In oxide films the decomposition of intermetallic compounds and formation of new compounds occurs with structural phase distortion. In the oxide films metallic the metallic iron particles α-Fe, iron oxide in the form of hematite α-Fe2O3, solid solutions of iron ions in ZrO2are formed. The phase composition of the oxide films depends on the alloy composition and changes during the growth process of the oxide film.