Preparation of porous carbons from polymeric precursors modified with acrylated kraft lignin

3rd International Conference on Competitive Materials and Technology Processes

Sobiesiak, M.^1

Department of Polymer Chemistry, Faculty of Chemistry, Maria Curie Sklodowska University, Lublin, Poland^1

关键词: Carbonaceous materials;    Nitrogen atmospheres;    Oxygen functional groups;    Polymeric precursors;    Specific interaction;    Suspension polymerization;    Textural properties;    Thermogravimetry analysis;   

Others  :  https://iopscience.iop.org/article/10.1088/1757-899X/123/1/012052/pdf
DOI  :  10.1088/1757-899X/123/1/012052

来源: IOP

【 摘 要 】

The presented studies concern the preparation of porous carbons from a BPA.DA-St polymer containing acrylated kraft lignin as a monomer. The porous polymeric precursor in the form of microspheres was synthesized in suspension polymerization process. Next samples of the polymer were impregnated with acetic acid or aqueous solution of acetates (potassium or ammonia), dried and carbonised in nitrogen atmosphere at 450°C. After carbonization microspherical shape of the materials was remained, that is desired feature for potential application in chromatography or SPE technique. Chemical and textural properties of the porous carbon adsorbents were characterized using infrared spectroscopy (ATR-FTIR), thermogravimetry analyses with mass spectrometry of released gases (TG-MS) and nitrogen sorption experiments. The presented studies revealed the impregnation is useful method for development of porous structure of carbonaceous materials. The highest values of porous structure parameters were obtained when acetic acid and ammonium acetate were used as impregnating substances. On the surface of the materials oxygen functional groups are present that is important for specific interactions during sorption processes. The highest contents of functionalities were observed for carbon BPA.DA-St-LA-C-AcNH4.