Characterisation of Suspension Precipitated Nanocrystalline Hydroxyapatite Powders

5th National Conference on Processing and Characterization of Materials

Mallik, P.K.^1 ; Swain, P.K.^1 ; Patnaik, S.C.^1

Department of Metallurgical and Materials Engineering, IGIT Sarang, Odisha, India^1

关键词: Conventional furnace;    Degree of aggregation;    Hydroxyapatite particles;    Hydroxyapatite powder;    Hydroxyapatite precipitates;    Nanocrystallines;    Reaction conditions;    Tissue replacement;   

Others  :  https://iopscience.iop.org/article/10.1088/1757-899X/115/1/012025/pdf
DOI  :  10.1088/1757-899X/115/1/012025

来源: IOP

【 摘 要 】

Hydroxyapatite (HA) is a well-known biomaterial for coating on femoral implants, filling of dental cavity and scaffold for tissue replacement. Hydroxyapatite possess limited load bearing capacity due to their brittleness. In this paper, the synthesis of nanocrystalline hydroxyapatite powders was prepared by dissolving calcium oxide in phosphoric acid, followed by addition of ammonia liquor in a beaker. The prepared solution was stirred by using magnetic stirrer operated at temperature of 80°C for an hour. This leads to the formation of hydroxyapatite precipitate. The precipitate was dried in oven for overnight at 100°C. The dried agglomerated precipitate was calcined at 800°C in conventional furnace for an hour. The influence of calcium oxide concentration and pH on the resulting precipitates was studied using BET, XRD and SEM. As result, a well-defined sub-rounded morphology of powders size of ∼41 nm was obtained with a salt concentration of 0.02 M. Finally, it can be concluded that small changes in the reaction conditions led to large changes in final size, shape and degree of aggregation of the hydroxyapatite particles.