Coated carbide drill performance under soluble coconut oil lubricant and nanoparticle enhanced MQL in drilling AISI P20 | |
Jamil, N.A.M.^1 ; Azmi, A.I.^1,2 ; Fairuz, M.A.^2 | |
School of Manufacturing Engineering, Universiti Malaysia Perlis (UniMAP), Pauh Putra Campus, Arau, Perlis | |
02600, Malaysia^1 | |
Faculty of Engineering Technology, Universiti Malaysia Perlis (UniMAP), UniCITI Alam, Padang Besar, Perlis | |
02100, Malaysia^2 | |
关键词: Coated carbide drills; Coconut oil; Cutting edges; Cutting speed; Image analysis software; Minimum quantity lubrication systems; Tool wear mechanism; Wear mechanisms; | |
Others : https://iopscience.iop.org/article/10.1088/1757-899X/114/1/012111/pdf DOI : 10.1088/1757-899X/114/1/012111 |
|
来源: IOP | |
【 摘 要 】
This research experimentally investigates the performance of a TiAlN coated carbide drill bit in drilling AISI P20 through two different kinds of lubricants, namely; soluble coconut oil (SCO) and nanoparticle-enhanced coconut oil (NECO) under minimum quantity lubrication system. The tool life and tool wear mechanism were studied using various cutting speeds of 50, 100 and 150 m/min with a constant feed of 0.01 mm/rev. Since the flank wear land was not regular along the cutting edge, the average flank wear (VB) was measured at several points using image analysis software. The drills were inspected using a scanning electron microscope to further elucidate the wear mechanism. The result indicates that drilling with the nanoparticle- enhanced lubricant was better in resisting the wear and improving the drill life to some extent.