The effect of heat treatment on the hardness and impact properties of medium carbon steel

2nd International Manufacturing Engineering Conference; 3rd Asia-Pacific Conference on Manufacturing Systems

Ismail, Noor Mazni^1 ; Khatif, Nurul Aida Amir^1 ; Kecik, Mohamad Aliff Kamil Awang^1 ; Shaharudin, Mohd Ali Hanafiah^1

Faculty of Manufacturing Engineering, Universiti Malaysia Pahang, Pekan

26600, Malaysia^1

关键词: Annealing process;    Effect of heat treatments;    Fractured surfaces;    Heat treatment process;    Medium-carbon steels;    Quenching and tempering;    Rockwell hardness;    Tempering process;   

Others  :  https://iopscience.iop.org/article/10.1088/1757-899X/114/1/012108/pdf
DOI  :  10.1088/1757-899X/114/1/012108

来源: IOP

【 摘 要 】

This paper covers the effect of heat treatment on the mechanical properties of medium carbon steel. The main objective of this project is to investigate the hardness and impact properties of medium carbon steel treated at different heat treatment processes. Three types of heat treatment were performed in this project which are annealing, quenching and tempering. During annealing process, the specimens were heated at 900°C and soaked for 1 hour in the furnace. The specimens were then quenched in a medium of water and open air, respectively. The treatment was followed by tempering processes which were done at 300°C, 450°C, and 600°C with a soaking time of 2 hours for each temperature. After the heat treatment process completed, Rockwell hardness test and Charpy impact test were performed. The results collected from the Rockwell hardness test and Charpy impact test on the samples after quenching and tempering were compared and analysed. The fractured surfaces of the samples were also been examined by using Scanning Electron Microscope. It was observed that different heat treatment processes gave different hardness value and impact property to the steel. The specimen with the highest hardness was found in samples quenched in water. Besides, the microstructure obtained after tempering provided a good combination of mechanical properties due to the process reduce brittleness by increasing ductility and toughness.