8th National Scientific Conference Advances in Electrotechnology (Postepy w Elektrotechnologii) | |
Corrosion resistance of the AISI 304, 316 and 321 stainless steel surfaces modified by laser | |
无线电电子学 | |
Szubzda, B.^1 ; Antoczak, A.^2 ; Koziol, P.^2 ; Lazarek, L.^2 ; Stpak, B.^2 ; Lcka, K.^2 ; Szmaja, A.^1 ; Ozimek, M.^1 | |
Electrotechnical Institute Division of Electrotechnology and Materials Science, M. Sklodowskiej-Curie 55/61, Wroclaw | |
50-369, Poland^1 | |
Institute of Telecommunications, Teleinformatics and Acoustics, Wroclaw University of Technology, Wybrzeze Wyspiaskiego 27, Wroclaw | |
50-370, Poland^2 | |
关键词: 321 Stainless Steel; Breakdown potential; Corrosion phenomena; Corrosion potentials; Electrochemical test; Nanosecond pulsed laser; Stainless steel surface; Structural tests; | |
Others : https://iopscience.iop.org/article/10.1088/1757-899X/113/1/012017/pdf DOI : 10.1088/1757-899X/113/1/012017 |
|
来源: IOP | |
【 摘 要 】
The article presents the analysis results of the influence of laser fluence on physical and chemical structure and corrosion resistance of stainless steel surfaces modified by irradiating with nanosecond-pulsed laser. The study was carried out for AISI 304, AISI 316 and AISI 321 substrates using Yb:glass fiber laser. All measurements were made for samples irradiated in a broad range of accumulated fluence (10400 J/cm2). The electrochemical composition (by EDX) and surface morphology (by SEM) of the prepared surfaces were carried out. Finally, corrosion resistance was analyzed by a potentiodynamic electrochemical test. The obtained results showed very high corrosion resistance for samples made by fluency of values lower than 100 J/cm2. In this case, higher values of corrosion potentials and breakdown potentials were observed. A correlation between corrosion phenomena, the range of laser power (fluence) and the results of chemical and structural tests were also found.