Deformation behavior of electro-deposited pure Fe and its texture evolution during cold-rolling and subsequent annealing

17th International Conference on Textures of Materials

材料科学;物理学

Sugiura, N.^1 ; Yoshinaga, N.^1 ; Ushioda, K.^1

Nippon Steel and Sumitomo Metal Corp, Futtsu, Japan^1

关键词: Annealing textures;    Cold rolling reduction;    Cold rolling textures;    Columnar structures;    Deformation behavior;    Oriented nucleation;    Recrystallization texture;    Texture evolutions;   

Others  :  https://iopscience.iop.org/article/10.1088/1757-899X/82/1/012053/pdf
DOI  :  10.1088/1757-899X/82/1/012053

学科分类：材料科学（综合）

来源: IOP

【 摘 要 】

Electro-deposited pure Fe has a characteristic of having very sharp isotropic ND// fiber texture with a needle-like shaped fine grain elongated to ND. This Fe exhibits a surprisingly high r-value of over 7; however, such a high r-value might not be rationalized only from texture. Careful slip analyses reveal that restricted slips take place in the specific {110} slip planes, which are perpendicular to the sheet surface. Since grain boundaries with columnar structure are also perpendicular to the sheet surface, the slip plane in a certain grain may easily connect to the slip plane in adjacent grains having within ±30 degree rotation relationship around the common axis of ND//. The operation of such a slip system is considered to cause the width strain much larger than the thickness strain. Furthermore, the texture evolution during cold-rolling and subsequent annealing was investigated using electro-deposited pure Fe as a starting material. Regardless of the amount of cold-rolling reduction, 65% to 90%, {111} cold-rolling texture developed. After recrystallization, {111} texture remained when material is cold-rolled by 65%, while {111} texture developed when materials are cold-rolled by 80% and 90%. From the investigation into the mechanism on the development of recrystallization texture, the oriented nucleation and selective growth theories are concluded to contribute to the evolution of annealing texture.