Effects of process parameters on microstructural evolution and properties of AZ61 alloy during hot extrusion

4th Global Conference on Materials Science and Engineering

Lu, Y.L.^1,2 ; Li, X.C.^1 ; Xu, W.T.^2 ; Wu, D.^2 ; Yang, M.^2

Key Construction Laboratory of Green Forming and Equipment from Jiangsu Province, Changzhou

213001, China^1

Jiangsu University of Technology, Changzhou

213000, China^2

关键词: Cleavage surfaces;    Deformation process;    Deformation temperatures;    Extrusion temperatures;    Fracture mechanisms;    Microstructures and properties;    Process parameters;    Severe plastic deformations;   

Others  :  https://iopscience.iop.org/article/10.1088/1757-899X/103/1/012037/pdf
DOI  :  10.1088/1757-899X/103/1/012037

来源: IOP

【 摘 要 】

Extrusion testing of AZ61 alloys were conducted at deformation temperatures of 300°C to 410°C and extrusion ratios of 3, 10 and 16 respectively to optimize the process parameters. The experimental results show that deformation process parameters significantly affect microstructures and properties. Optical microscope observation shows that grains are refined greatly during hot extrusion and the mechanical properties are improved with increasing the extrusion ratio. For AZ61 alloy, the optimal extrusion temperature is 370°C. When deformation temperature increases, more slip systems participate in the plastic deformation, which leads to the decrease of the cleavage surface. After severe plastic deformation, a remarkable improvement of ductility of AZ61 alloy has been found. The ductile fracture mechanism is gradually dominant instead of brittle fracture with increasing the extrusion ratio.