Contribution of shear deformation to grain refinement and densification of iron powder consolidated by high pressure torsion

6th International Conference on Nanomaterials by Severe Plastic Deformation

材料科学;化学

Zhao, Y.J.^1 ; Massion, R.^1,2 ; Grosdidier, T.^1,2 ; Toth, L.S.^1,2

Laboratoire d'Etude des Microstructures et de Mécanique des Matériaux (LEM3), Université de Lorraine, Ile du Saulcy, 57045 Metz, France^1

Laboratory of Excellence on Design of Alloy Metals for Low-mAss Structures (DAMAS), Université de Lorraine, Ile du Saulcy, 57045 Metz, France^2

关键词: Electron back-scattered diffraction;    Grain size distribution;    High pressure torsions;    Homogeneous microstructure;    Microstructure investigations;    Powder consolidations;    Texture evolutions;    Texture measurement;   

Others  :  https://iopscience.iop.org/article/10.1088/1757-899X/63/1/012032/pdf
DOI  :  10.1088/1757-899X/63/1/012032

学科分类：材料科学（综合）

来源: IOP

【 摘 要 】

High Pressure Torsion (HPT) experiments were performed for consolidation of water-atomized pure iron powder (99%) with initial particle sizes of 20-100 gm. The experiments were carried out successfully at room temperature, achieving both low level of residual porosity and significant grain refinement, thanks to the intense shear strain and hydrostatic pressure applied in HPT. X-ray diffraction analysis was carried out on the consolidated samples which revealed no significant proportion of oxides. Considering the inherent heterogeneity of the imposed shear strain in HPT, different positions across the diameters of sample disks were selected for mechanical property and microstructure investigations. The effect of shear deformation on the microstructure and texture was investigated by metallography, scanning electron microscopy, electron backscattered diffraction (EBSD). The micro-hardness and porosity of the samples as a function of shear strain at constant hydrostatic pressure were also measured. The grain size distributions showed homogeneous microstructures with significant grain refinement due to shear deformation. The texture measurements revealed that a shear texture typical to the shear of bcc iron was obtained during HPT compaction of iron powder.