Effect of compatibilizing agents on the interface and mechanical behaviour of polypropylene/hemp bast fiber biocomposites

2015 Global Conference on Polymer and Composite Materials

材料科学;化学

Boruvka, M.^1 ; Lenfeld, P.^1 ; Brdlik, P.^1 ; Behalek, L.^1

Technical University of Liberec, Department of Engineering Technology, Studentska 2, Liberec

46117, Czech Republic^1

关键词: Automotive composites;    Bio-based polymers;    Compatibilizing agents;    Hydrophilic fibers;    Hydrophobic polymers;    Mechanical behaviour;    Twin screw extrusion;    Weight percentages;   

Others  :  https://iopscience.iop.org/article/10.1088/1757-899X/87/1/012085/pdf
DOI  :  10.1088/1757-899X/87/1/012085

学科分类：材料科学（综合）

来源: IOP

【 摘 要 】

During the last years automotive industry has given a lot of attention to the biobased polymers that are sustainable and eco-friendly. Nevertheless fully green composites are currently too expensive for most applications. A viable solution and logical starting point at this material revolution lies in reinforced synthetic thermoplastics based on plant derived biodegradable fibers. Plant fibers (PF's) have potential to reduce weight of composite vehicle parts up to 40% compared with the main automotive composites filler, glass fibers (GF's). Production of GF's composites is much more energy intensive and polluting compared with growing, harvesting and preparing of PF's. The main disadvantage of PF's lies in combination of non-polar hydrophobic polymer matrix and polar hydrophilic fibers. This combination creates poor interface with low adhesion of both components. That implies poor wettability of fibres by polymer matrix and low mechanical properties of biocomposites. Therefore specific compatibilizing agents (Struktol SA1012, Fusabond P353, Smart + Luperox) were used in order to enhance compatibility between reinforcement and matrix. In this paper sets of biocomposite compounds were prepared by twin screw extrusion considering different type and weight percentage (wt. %) of compatibilizing agents, hemp bast fibres (HBF's) within ratio 20 (wt. %) and polypropylene (PP) THERMOFIL PP E020M matrix. Resulting compounds were than injection molded and tested samples were characterized by means of scanning electron microscopy (SEM) and mechanical testing.