Dielectric properties of BaTiO3 based materials with addition of transition metal ions with variable valence

International Conference on Functional Materials and Nanotechnologies 2013

材料科学;物理学

Sitko, D.^1 ; Bk, W.^1 ; Garbarz-Glos, B.^1 ; Budziak, A.^2 ; Kajtoch, C.^1 ; Kalvane, A.^3

Institute of Physics, Pedagogical University of Cracow, Poland^1

H. Niewodniczanski Institute of Nuclear Physics PAN, Cracow, Poland^2

Institute of Solid State Physics, University of Latvia, Latvia^3

关键词: Electric modulus;    Electrical permittivity;    Frequency ranges;    Imaginary parts;    Single-phase compound;    Temperature range;    Tetragonal structure;    Uniform distribution;   

Others  :  https://iopscience.iop.org/article/10.1088/1757-899X/49/1/012050/pdf
DOI  :  10.1088/1757-899X/49/1/012050

学科分类：材料科学（综合）

来源: IOP

【 摘 要 】

Dielectric properties of BaTiO3(BT), BaTiO3+0.1wt. %MnO2(BTMn) and BaTiO3+0.1wt.%Fe2O3(BTFe) solid solution was investigated. The effects of substitution on the microstructure and on the electric properties of BaTiO3samples were studied by performing X-ray diffraction and electric measurements. X-ray diffraction analysis of the samples shows the formation of single-phase compound with a tetragonal structure at room temperature. SEM microphotographs exhibit the uniform distribution of grains. The electric properties (a real part of electrical permittivity(') and an imaginary part of electric modulus (M")) were investigated in the temperature range from 150K to 600K and in the frequency range from 0.1 Hz to 10 MHz. It was found that a Fe and Mn ions -doping influence the electric properties of the investigated polycrystalline materials.