Multilayered nanocrystalline CrN/TiAlN/MoS2 tribological thin film coatings: preparation and characterization

2nd International Conference on Competitive Materials and Technological Processes

Papp, S.^1 ; Kelemen, A.^1 ; Jakab-Farkas, L.^1 ; Vida-Simiti, I.^2 ; Biró, D.^1

Sapientia University, Cluj Napoca, Faculty of Technical and Human Sciences, Sighisoarei Road 1/C, 540485 Tirgu-Mures, Romania^1

Technical University of Cluj Napoca, Faculty of Materials Science and Engineering, Department of Materials Science and Technology, Muncii Avenue 103-105, 400641 Cluj-Napoca, Romania^2

关键词: Auger electron spectroscopies (AES);    Chemical compositions;    Cross-sectional transmission electron microscopy;    Microstructure investigations;    Multilayer coating structures;    Nanocrystalline multilayer;    Reactive co-sputtering;    Reactive sputtering process;   

Others  :  https://iopscience.iop.org/article/10.1088/1757-899X/47/1/012016/pdf
DOI  :  10.1088/1757-899X/47/1/012016

来源: IOP

【 摘 要 】

Nanocrystalline multilayer thin film coatings, composed of nanometer-scale thick CrN, TiAlN and MoS2tri-layer systems, were prepared by reactive co-sputtering processes. The self-lubricated multilayer coating structures were deposited by one-fold oscillating movement of substrates in front of the sputter sources. Three independently operated direct current (dc) excited unbalanced magnetrons (UM) with rectangular cathodes of TiAl alloy (50/50%), pure chromium and MoS2were used as sputter sources. The reactive sputtering process was performed in a mixture of Ar-N2atmosphere. Hardened high-speed-steel (HSS) and thin oxide covered Si (100) wafers were used as substrates for tribological- and microstructure investigations, respectively. According to results of the chemical composition evaluated by Auger-electron spectroscopy (AES) and microstructure investigation by cross sectional transmission electron microscopy (XTEM), the CrN, TiAlN and the MoS2phases form practically continuous layers with large gradient transition of composition. The as-deposited CrN/ (Al,Ti)N/MoS2coatings have shown good friction behaviour, tested at room temperature in dry sliding condition with a ball-on-disk tribometer.