Effect of Acetylene Black Content in Li4Ti5O12 Xerogel Solid-State Anode Materials on Half-Cell Li-ion Batteries Performance

International Conference on Energy Sciences 2016

能源学;物理学

Abdurrahman, N.M.^1 ; Priyono, B.^1 ; Syahrial, A.Z.^1 ; Subhan, A.^2

Departement of Metallurgical and Materials Engineering, Universitas Indonesia, Depok

16424, Indonesia^1

Research Center for Physics-LIPI, PUSPIPTEK, Tangerang, Banten

15310, Indonesia^2

关键词: Active material content;    Battery performance;    Brunauer emmett tellers;    Charge discharge tests;    Counter electrodes;    Discharge capacities;    Electrode surfaces;    Li-ion batteries anodes;   

Others  :  https://iopscience.iop.org/article/10.1088/1742-6596/877/1/012008/pdf
DOI  :  10.1088/1742-6596/877/1/012008

来源: IOP

【 摘 要 】

The effect of Acetylene Black (AB) additive contents in lithium titanate/Li4Ti5O12(LTO) anode on Li-ion Batteries performance is studied in this work. The LTO active material for Li-ion batteries anode was successfully synthesized using sol-gel method to form TiO2xerogel continued by mixing process with LiOH in ball-mill and then sintered to obtain spinel LTO. The LTO powder is characterized by X-Ray Diffraction (XRD), scanning electron microscopy-Energy Dispersive Spectroscopy (SEM-EDS), and Brunauer-Emmett-Teller (BET). The spinel LTO and TiO2 rutile were detected by XRD diffractogram. The LTO powder is in the form of agglomerates structure. This powder then was mixed with PVDF binder (10%wt) and AB additives with various amount from 10%wt (LTO2 Ac-1), 12%wt (LTO2 Ac-2), and 15%wt (LTO2 Ac-3) of total weight solid content to form electrode sheet. Half-cell coin battery was made with lithium metal foil as a counter electrode. Cyclic voltammetry (CV), Electrochemical-impedance spectroscopy (EIS), and charge discharge (CD) test used to examine the battery performance. The highest resistance value is obtained in LTO2 Ac-3 sample with 15%wt of AB. It might be caused by the formation of side reaction product on electrode surface at initial cycle due to high reactivity of LTO2 Ac-3 electrode. The highest initial capacity at CV test and CD test was obtained in LTO2 Ac-1 (10%wt AB) sample, due to the best proportion of active material content in the compound. While, in the charge-discharge test at high current rate, the best sample rate-capability performance belongs to LTO2 Ac-3 sample (15%wt AB), which still have 24.12 mAh/g of discharge capacity at 10 C with 71.34% capacity loss.