2nd Colombian Congress of Electrochemistry; 2nd Symposium on Nanoscience and Nanotechnology | |
Characterization of mechanical properties and electrochemical behaviour in a Hank?s solution of 316L/Cr1- xAlxN system | |
物理学;化学 | |
Osorio, D.M.^1 ; Caicedo, J.C.^1 ; Aperador, W.^2 ; Benitez-Castro, A.M.^3 ; Giraldo-Betancur, A.L.^3 ; Muñoz-Saldaña, J.^3 ; Yañez-Limón, J.M.^3 ; Sanchez, O.^4 ; Zambrano, G.^1 | |
Universidad Del Valle, Cali, Colombia^1 | |
Universidad Militar Nueva Granada, Bogotá, Colombia^2 | |
Centro de Investigación y de Estudios Avanzados, Instituto Politécnico Nacional, Querétaro, Mexico^3 | |
Servicio Nacional de Aprendizaje, Cali, Colombia^4 | |
关键词: 316 L stainless steel; Biomedical applications; Crystallographic orientations; Deposited coatings; Electrochemical behaviour; Hank's solution; Reactive magnetron co-sputtering; Simulated body fluids; | |
Others : https://iopscience.iop.org/article/10.1088/1742-6596/786/1/012037/pdf DOI : 10.1088/1742-6596/786/1/012037 |
|
来源: IOP | |
【 摘 要 】
Cr1-xAlxN hard coatings were successfully deposited by R.F. reactive magnetron co-sputtering in an Ar/N2 gas mixture using chromium and aluminium targets on 316L stainless steel substrates. Crystallographic orientations associated to the Cr1-xAlxN FCC based in the conjugate complex of CrN and w-AlN phases, with ao=4.18Å lattice parameter for the ternary Cr1-xAlxN compound were identified by X-Ray diffraction. The thickness and roughness of the deposited coatings are 1.00±0.05nm and 2.65±0.6nm, respectively. The mechanical properties were determined by nanoindentation leading to a hardness of 27.8±2.6GPa and elastic modulus of 346GPa. The corrosion resistance of the coated 316L/Cr1-xAlxN system under simulated body fluid (SBF, Hank's solution) was determined via electrochemical impedance spectroscopy. A reduction in the corrosion rate of 99% in relation to uncoated 316L stainless steel substrate was found by Tafel. Thus, these coatings seem to be excellent candidates to be used in biomedical applications.【 预 览 】