Borax as flux on sintering of iron Ancor Steel 1000? under glow discharge

3rd International Meeting for Researchers in Materials and Plasma Technology; 1st Symposium on Nanoscience and Nanotechnology

物理学;材料科学

Suarez, H.G. Ariza^1 ; Santos, A Sarmiento^1 ; Otálora, C.A. Ortiz^1

Universidad Pedagógica y Tecnológica de Colombia, Tunja, Colombia^1

关键词: Abnormal glow discharge;    Fusion process;    Low pressures;    Powder metallurgical;    Reducing atmosphere;    Sample density;    Sintered samples;    Sintering temperatures;   

Others  :  https://iopscience.iop.org/article/10.1088/1742-6596/687/1/012083/pdf
DOI  :  10.1088/1742-6596/687/1/012083

学科分类：材料科学（综合）

来源: IOP

【 摘 要 】

This work studies the flux effect of borax (di sodium tetraborate decahydrate) on sintering of iron Ancor Steel 1000®in abnormal glow discharge. The incidence of the percentage by weight of borax and the sintering temperature in the process were observed. Samples of powder metallurgical iron were prepared with proportions of 0.50%, 2.0%, 4.0% and 6.0% by weight of borax using the procedures of powder metallurgy. The samples were sintered at 800 and 1100°C for 30min, by glow discharge at low pressure in a reducing atmosphere composed of 20% H2+80% Ar. The samples in compact green-state were analyzed by TGA-DSC to determine the fusion process and mass loss during sintering. The analysis of microhardness and density, shows that at a sintering temperature of 800°C the sample density decreases and the sample microhardness increases with respect to sintered samples without borax. Sintered samples were analysed by DRX showing the absence of precipitates.