The influence of peak shock stress on the high pressure phase transformation in Zr

18th APS-SCCM; 24th AIRAPT

Cerreta, E.K.^1 ; Addessio, F.L.^1 ; Bronkhorst, C.A.^1 ; Brown, D.W.^1 ; Escobedo, J.P.^1 ; Fensin, S.J.^1 ; Gray, G.T.^1 ; Lookman, T.^1 ; Rigg, P.A.^1 ; Trujillo, C.P.^1

Los Alamos National Laboratory, Los Alamos

NM

87545, United States^1

关键词: Alpha phase;    Equilibrium phase diagrams;    Hexagonal close packed;    High pressure;    High pressure phase transformations;    Shock conditions;    Shock loadings;    Shock stress;   

Others  :  https://iopscience.iop.org/article/10.1088/1742-6596/500/3/032003/pdf
DOI  :  10.1088/1742-6596/500/3/032003

来源: IOP

【 摘 要 】

At high pressures zirconium is known to undergo a phase transformation from the hexagonal close packed (HCP) alpha phase to the simple hexagonal omega phase. Under conditions of shock loading, a significant volume fraction of high-pressure omega phase is retained upon release. However, the hysteresis in this transformation is not well represented by equilibrium phase diagrams and the multi-phase plasticity under shock conditions is not well understood. For these reasons, the influence of peak shock stress and temperature on the retention of omega phase in Zr has been explored. VISAR and PDV measurements along with post-mortem metallographic and neutron diffraction characterization of soft recovered specimens have been utilized to quantify the volume fraction of retained omega phase and qualitatively understand the kinetics of this transformation. In turn, soft recovered specimens with varying volume fractions of retained omega phase have been utilized to understand the contribution of omega and alpha phases to strength in shock loaded Zr.