Repair effect of magnesium phosphate cement and carbon fiber cloth on concrete structure

2018 International Conference on Civil and Hydraulic Engineering

土木建筑工程;水利工程

Kejia, Luo^1 ; Chengyou, Wu^1 ; Baikiin, Chen^1 ; Panpan, Liu^1 ; Ruiyang, Pang^1 ; Yuwen, Lu^1

School of Civil Engineering, Qinghai University, Xining

810016, China^1

关键词: Calcination temperature;    Calcination time;    Carbon fiber cloths;    Concrete repairs;    Magnesium phosphate cement;    Potassium dihydrogen phosphate;    Roasting temperature;    Water-cement ratio;   

Others  :  https://iopscience.iop.org/article/10.1088/1755-1315/189/3/032016/pdf
DOI  :  10.1088/1755-1315/189/3/032016

学科分类：土木及结构工程学

来源: IOP

【 摘 要 】

Magnesium phosphate cement (MKPC) is a useful by product from the extraction of lithium from salt lake brine (MS) and potassium dihydrogen phosphate(KH2PO4). The effects of roasting temperature, ratio, water-cement ratio and fly ash on the performance of magnesium phosphate cement were studied. The application of potassium magnesium phosphate cement in concrete repair and reinforcement in combination with carbon fiber cloth as a concrete reinforcement were also studied. Experimental results show that when the calcination temperature is at 1100°C, the calcination time is 1 hour, & when the mass ratio of magnesium oxide to potassium dihydrogen phosphate is 2:1, water-cement ratio is 0.2, and fly ash is 30%, the carbon fiber cloth improves the concrete beam's load carrying capacity, flexural strength, as well as delay the appearance of concrete cracks and extension.