A study on super-sulfated cement using Dinh Vu phosphogypsum

2nd International Conference on Sustainable Development in Civil, Urban and Transportation Engineering

地球科学;运输工程;经济学

Lam, Nguyen Ngoc^1

National University of Civil Engineering, Hanoi, Viet Nam^1

关键词: Carbon emissions;    Cementitious materials;    Diammonium phosphates;    Environmental-friendly;    Fertilizer plant;    Ground granulated blast furnace slag;    Industrial zones;    Ordinary Portland cement;   

Others  :  https://iopscience.iop.org/article/10.1088/1755-1315/143/1/012016/pdf
DOI  :  10.1088/1755-1315/143/1/012016

来源: IOP

【 摘 要 】

Super-sulfated cement (SSC) is a newly developed unburnt cementitious material. It is a kind of environmental-friendly cementitious material due to its energy-saving, carbon emission reducing, and waste-utilization. It mainly composes of phosphogysum (PG) and ground granulated blast furnace slag (GFS), with a small amount of cement. In Vietnam, the Diammonium Phosphate DAP - Dinh Vu fertilizer plant in Dinh Vu industrial zone in the northern port city of Hai Phong - has discharged millions of tons of solid waste containing gypsum after 9 years of operation. The waste has changed the color of the water, eroded metal and destroyed fauna and floral systems in the surrounding area. Notably, according to the environmental impact assessment, the gypsum landfill area is supposed to be 13 hectares and the storage time reaches up to five years. This paper presents the experimental results on SSC using a high amount of Dinh Vu phosphogypsum and GFS in comparison with those of ordinary Portland cement (PC). The results show that the setting time of SSC is much longer than that of Portland cement but the compressive strength of SSC can be obtained 45-50 MPa at the age of 28 days, similar to that of the control sample using 100% PC40, and 69MPa at the age of 90 days. This value even exceeds the compressive strength of the PC40 cement.