The Influence of Calcium Carbonate Composition and Activated Carbon in Pack Carburizing Low Carbon Steel Process in The Review of Hardness and Micro Structure

International Conference on Environment and Technology 2017

生态环境科学

Hafni, H.^1 ; Hadi, Syafrul^1 ; Edison, E.^1

Mechanical Engineering Department, Padang Institute of Technology, Padang, Indonesia^1

关键词: Average values;    Carburizing furnaces;    Carburizing process;    Critical temperatures;    Diffusion of carbons;    High carbon content;    Holding time;    Refractory bricks;   

Others  :  https://iopscience.iop.org/article/10.1088/1755-1315/97/1/012037/pdf
DOI  :  10.1088/1755-1315/97/1/012037

学科分类：环境科学（综合）

来源: IOP

【 摘 要 】

Carburizing is a way of hardening the surface by heating the metal (steel) above the critical temperature in an environment containing carbon. Steel at a temperature of the critical temperature of affinity to carbon. Carbon is absorbed into the metal form a solid solution of carbon-iron and the outer layer has high carbon content. When the composition of the activator and the activated charcoal is right, it will perfect the carbon atoms to diffuse into the test material to low carbon steels. Thick layer of carbon Depending on the time and temperature are used. Pack carburizing process in this study, using 1 kg of solid carbon derived from coconut shell charcoal with a variation of 20%, 10% and 5% calcium carbonate activator, burner temperature of 9500C, holding time 4 hours. The test material is low carbon steel has 9 pieces. Each composition has three specimens. Furnace used in this study is a pack carburizing furnace which has a designed burner box with a volume of 1000 x 600 x 400 (mm3) of coal-fired. Equipped with a circulation of oxygen from the blower 2 inches and has a wall of refractory bricks. From the variation of composition CaCO3, microstructure formed on the specimen with 20% CaCO3, better diffusion of carbon into the carbon steel, it is seen by the form marten site structure after quenching, and this indicates that there has been an increase of or adding carbon to in the specimen. This led to the formation of marten site specimen into hard surfaces, where the average value of hardness at one point side (side edge) 31.7 HRC.