Thermal Cyclic Resistance Polyester Resin Composites Reinforce Fiber Nut Shell

International Conference on Environment and Technology 2017

生态环境科学

Fahmi, Hendriwan^1

Institut Teknologi Padang, Padang

25146, Indonesia^1

关键词: Bending properties;    Cyclic resistance;    Long fiber;    Nut-shells;    Resin composites;    Thermal Cyclic;    Three-point bending test;    Universal testing machines;   

Others  :  https://iopscience.iop.org/article/10.1088/1755-1315/97/1/012036/pdf
DOI  :  10.1088/1755-1315/97/1/012036

学科分类：环境科学（综合）

来源: IOP

【 摘 要 】

The purpose of study is to determine the effect of fiber length and thermal cyclic of the bending strength of polyester resin composite reinforced by fibers nut shell. The materials used in this study is a nut shell fibers with fiber length of 1 cm, 2 cm and 3 cm and polyester resin with composition 70-30%wt. Fiber nut shell treated soaking in NaOH 30% for 30 minutes, then rinse with clean water so that the fiber free of alkali and then dried. Furthermore, the composite is heated in an oven to a temperature of 100°C for 1 hour and then cooled in the open with a variety of thermal cyclic 30, 40, and 50 times. Bending properties of composites known through the testing process using a three-point bending test equipment universal testing machine. The test results show that the bending strength bending highest in fiber length of 3 cm with 30 treatment cycles of thermal to the value of 53.325 MPa, while the lowest occurred in bending strength fiber length of 1 cm with no cycles of thermal treatment to the value of 30.675 MPa.